Hi-Build Vinyl 1lt Semi-Matt Black Paint
- Inteded Use:
- Metal Finishing
- A rapid dry 'one coat' anti corroci9ve silf priming low sheen topcoat, giving a tough flexable film with remarkable adhesion to many difficult substrates with excellen re-coat characteristics.
- General metal fabrication; used to overcome problems associated with conventional alkyd paints subject to severe exposure conditions often associated with poor adhesion.
Metal railings and fencing; adheres directly to galvanised metal or steel with no need for mordant solution or etch primers. To ensure white zinc salts do not migrate through the coatings apply 75 microns dft and in a coastal enviroment at 120 microns dft.
Metalwork subject to low temperatures, High Build Vinyl remains flexible
Metalwork subject to high humidity
- Articles - that are not part of a building structure (and therefore outside of the scope of the building products VOC Product Directive)
Inside Building: Machinery, fixed plant, moveable equipment, fork lift trucks, trolleys, frames, guards, etc.
- Outside Building: Exterior surfaces of tanks, pipework and process plant, towers, bridges or any structure which is not part of a building
- Some rigid and flexable plastics; such as Foamex and PVC. Always test prior to painting. Seek advice from MDA Bitec if required
- Suitable Substrates and Preperation
- Untreated steel and wrought ironwork; for best results blast clear prior to painting to SA 2 1/2, otherwise manually abrade using powered hand tools and abrasives to ST2
- Weathered Galvanised Steel; remove all traces of oil or grease, lightly abrade with P600 wet or dry paper. Remove Rust.
- Heavy Chromated Galvanised Steel; alkali clean and then proceed as for Bright Spangled Galvanised Steel
- Bright Galvanised Steel and Newley Galvanised Steel (less than 6 months since galvanising); remove oil or grease, throughly abrade with P600 wet or dry, remove dust.
- Aluminium; use 1 Pack Etch Primer CT
- Always Prepare a test area
- Other Substrate seek advice from MDA Bitec
- Product Information:
- Volume Solids: 31%
Weight Solids: 43%
Typical film thickness: 242 microns wet film thickness to give 75 microns dry film thickness
Theoretical Coverage: 4.1sq meters/litre at 75 microns dry film thickness
- Drying and Recoating: (aprocimate drying times at 50 microns d.f.t)
- Sustrate Temperature:
- 10ºC
- Touch Dry in 45 Minutes
Overcoating in 2 hours (Minimum)
- Touch Dry in 20 Minutes
Overcoating in 1 hour (Minimum)
Additional Information
| Manufacturer | MANOR |
|---|---|
| Brand | Manor |
| Make | Pro Range |
| Manufacturer Part Number | HBVBK-1LT |